SUPERNOVA SLICKLINE
Service Providers around the world are benefiting from the excellent corrosion resistance, high minimum break loads and cost savings provided by Supernova Slicklines.
FUSHUN’s vast experience, wire drawing expertise and technical knowledge across a wide range of stainless steel and nickel alloys enables slickline users to benefit from competitive prices and short lead times without compromising product quality, service performance or line life. Benefits which are further extended by the introduction of our Supernova 100 grade. All our slicklines are manufactured in Switzerland using raw materials from European producers; all lines are 100% Eddy Current Tested (NDT) and free from welds.
W. Nr. : 1.4401 / AISI: UNS S31600
• is suitable for use in Low Corrosive Conditions
• can be used in up to 35% of CO2 (with zero H2S)
• can be used in Low Chloride Conditions of up to 3.5%
• can be used in High Temperature – up to 150°C.
W. Nr. : 1.4462 / AISI: UNS S32205
• very good in Chloride Conditions of up to 30% (with zero H2S)
• very good in high CO2 Conditions of up to 30% (with zero H2S)
• can be used in High Temperature – up to 150° C.
AISI: UNS S31254
• hot & sour (H2S + Chlorides) with high CO2
• concentrations of up to 25% Chloride with H2S and CO2
• can be used in High Temperature – up to 250°C
• All Concentrations of H2S + CO2 .
W. Nr. : 1.4529 / AISI: UNS N08926
• hot & sour (H2S + Chlorides) with high CO2
• concentrations of up to 30% Chloride with H2S and CO2
• can be used in High Temperature – up to 250°C
• All Concentrations of H2S + CO2 .
W. Nr. : 1.4501 / AISI: UNS S32760
• high mechanical properties whilst retaining good ductility
• excellent resistance to acid corrosion and crevice corrosion
• high resistance to abrasion, fatigue and corrosion fatigue
• excellent resistance to chloride and sulphide stress corrosion cracking.
Grades & chemical composition
| C | Mn | Si | S | P | Ni | Cr | Mo | Cu | N | W | PRE | |
|
S31600 |
- | - | - | - | - | 10.00 min | 16.50 min | 2.00 min | - | 0.03 min | - |
23.5 - 27 |
| 0.08 max | 2.00 max | 1.00 max | - | - | 13.80 max | 18.00 max | 2.60 max | - | 0.06 max | - | ||
|
S32205 |
- | - | - | - | - | 4.50 min | 21.00 min | 2.50 min | - | 0.15 min | - |
31.65 - 37 |
| 0.03 max | 2.00 max | 1.00 max | - | - | 6.00 max | 23.00 max | 3.40 max | - | 0.20 max | - | ||
|
S31254 |
- | - | - | - | - | 17.50 min | 19.50 min | 6.00 min | 0.50 min | 0.15 min | - |
42 - 46 |
| 0.02 max | 1.00 max | 0.80 max | - | - | 18.50 max | 21.00 max | 6.50 max | 1.00 max | 0.25 max | - | ||
|
N08926 |
- | - | - | - | - | 24.50 min | 19.50 min | 6.00 min | 0.85 min | 0.12 min | - |
43 - 46 |
| 0.02 max | 1.00 max | 0.80 max | - | 26.00 max | 21.00 max | 6.70 max | 1.00 max | 0.20 max | - | |||
|
S32760 |
- | - | - | - | - | 6.00 min | 24.00 min | 3.00 min | 0.50 min | 0.20 min | 0.50 min |
> 41 |
| 0.03 max | 1.00 max | 1.00 max | 0.015 max | 0.03 max | 8.00 max | 26.00 max | 4.00 max | 1.00 max | 0.30 max | 1.00 max |
Standard diameters
0.092”/ 0.108”/ 0.125”/ 0.140”/ 0.160”(tolerance +/-0.001”)
Standard lengths
20.000 feet / 25.000 feet. / 30.000 feet
Mechanical properties
| Novametal | Diameter | Min Breaking Load | Min Tensile Strength | Wt / 1000 Ft. | RSL |
|
S31600 |
0.092” | 1420 lbf | 1460 N/mm2 | 22.64 lbs | 75% |
| 0.108” | 1940 lbf | 1440 N/mm2 | 31.20 lbs | 75% | |
| 0.125” | 2530 lbf | 1420 N/mm2 | 41.80 lbs | 75% | |
| 0.140” | 3130 lbf | 1410 N/mm2 | 53.00 lbs | 75% | |
| 0.160” | 4050 lbf | 1380 N/mm2 | 69.00 lbs | 75% | |
|
S32205 |
0.092” | 1630 lbf | 1690 N/mm2 | 22.48 lbs | 75% |
| 0.108” | 2190 lbf | 1620 N/mm2 | 30.95 lbs | 75% | |
| 0.125” | 2850 lbf | 1550 N/mm2 | 41.49 lbs | 75% | |
| 0.140” | 3500 lbf | 1530 N/mm2 | 52.10 lbs | 75% | |
| 0.160” | 4200 lbf | 1480 N/mm2 | 68.03 lbs | 75% | |
|
S31254 |
0.092” | 1610 lbf | 1650 N/mm2 | 23.30 lbs | 75% |
| 0.108” | 2120 lbf | 1600 N/mm2 | 32.00 lbs | 75% | |
| 0.125” | 2650 lbf | 1490 N/mm2 | 42.90 lbs | 75% | |
| 0.140” | 3130 lbf | 1410 N/mm2 | 54.10 lbs | 75% | |
| 0.160” | 3920 lbf | 1380 N/mm2 | 70.00 lbs | 75% | |
|
N08926 |
0.092” | 1580 lbf | 1640 N/mm2 | 23.31 lbs | 75% |
| 0.108” | 2170 lbf | 1635 N/mm2 | 32.00 lbs | 75% | |
| 0.125” | 2900 lbf | 1630 N/mm2 | 42.90 lbs | 75% | |
| 0.140” | 3480 lbf | 1560 N/mm2 | 54.10 lbs | 75% | |
| 0.160” | 4440 lbf | 1530 N/mm2 | 70.00 lbs | 75% | |
|
S32760 |
0.092” | 1920 lbf | 1954 N/mm2 | 22.10 lbs | 75% |
| 0.108” | 2380 lbf | 1800 N/mm2 | 30.55 lbs | 75% | |
| 0.125” | 3200 lbf | 1820 N/mm2 | 41.03 lbs | 75% | |
| 0.140” | 4050 lbf | 1793 N/mm2 | 51.54 lbs | 75% | |
| 0.160” | 5150 lbf | 1748 N/mm2 | 67.45 lbs | 75% | |
| RSL (Recommended Safe Load) = 75% of Effective Break Load / EBL (Effective Break Load) = Actual measured BL minus weight of tools and wire in use | |||||