Product Details:
|
Thickness: | 0.1 To 6 Mm | Width: | 10 To 400 Mm |
---|---|---|---|
Delivery Condition: | Annealed Or Annealed And Skin Passed; Cold Rolled(+CR); Spheroidized Carbides(+AC) | Surface Condition: | Bright |
Steel Grade: | 1035 | Form: | Steel Coils Strips |
Standard: | ASTM A684 1035 | ||
Highlight: | ASTM A684 1035 Carbon Steel Strip,1035 Cold Rolled Spring Steel Strip |
We stock a large range of carbon steels which can be slit to the customers requirement. We also have a wide range of excess offcuts which may be of interest.
High Carbon Steel Strip can be produced to a large variety of tensile strengths/hardnesses to suit the subsequent component-manufacturing processes and end-uses involved. The softened/annealed condition provides maximum deformability for more complex component shapes or, alternatively, lower relative wear on component-forming tools. In this condition hardnesses of 160 - 200 VPN (equivalent to tensile strength up to about 690 N/mm²) would be typical.
Thickness: 0.01-6mm
Tolerances on thickness: +/-0.015 - 0.030mm
Tolerances on width: +/- 0.10 - 0.30 mm
Tolerances on length of cut-to-Iength: -0/+10-30mm
Steel Designation No. | Carbon | Manganese | Phosphorus, max | Sulfur, max |
1035 | 0.32 to 0.38 | 0.60 to 0.90 | 0.030 | 0.035 |
Silicon composition as one of the following:
Type 1: 0.15-0.30
Type 2: 0.10 max
Condition:
1 The strip shall be furnished cold rolled spheroidized annealed, soft annealed, intermediate hardness, or full hard, as specified.
2 Intermediate hardness may be obtained by either rolling the strip after final annealing or by varying the annealing treatment, or both.
3 Pinch Pass一Spheroidized annealed and annealed material may be pinch rolled after the final anneal to improve flatness, uniformly oil, modify surface, obtain proper mechanical properties, and minimize stretcher strains if required by the purchaser.
1 Soft spheroidized annealed high-carbon steel is intended for applications requiring maximum cold forming. It is normally produced to give the lowest maximum Rockwell hardness for each grade.
2 Soft annealed high-carbon steel is intended for applications requiring moderate cold forming. It is produced to a maximum Rockwell hardness.
3 Intermediate hardness high-carbon steel is intended for applications where cold forming is slight or a stiff, springy product is needed, or both. It is produced to specified Rockwell hardness ranges, the maximum being higher than obtained for the annealed type.
4 Full hard high-carbon steel is intended for flat applications. It is produced to minimum Rockwell hardness requirements, which vary with grade, microstructure and gauge. Full hard can be produced with either a pearlitic or spheroidized microstructure or a mixture of both. The minimum hardness should be established between the consumer and the producer.
Surface—The strip shall be furnished with a No. 2 Regular Bright or No. 1 Matte (Dull) finish, as specified.
Oiling—The strip shall be furnished oiled or dry, as specified.
Carbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% silicon and 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium and nickel are present in these steels.
AISI 1035 is a water resisting carbon steel whose wear resistance and hardenability are increased by the addition of small quantity of chromium.
SAE-AISI 1035 steel is a carbon (non-alloy) steel formulated for primary forming into wrought products. 1035 is the designation in both the SAE and AISI systems for this material. G10350 is the UNS number.
The following are the major applications of AISI 1035 carbon steel:
Levers
Bolts
Nuts
Studs
1 Cutting: Small pieces
2 CNC Machine: Produce as your drawing
3 Package: Bare/Nylon/Canvas/Wooden
4 Payment:T/T, L/C, O/A(request credit)
5 Transport:FOB/CFR/CIF/DDU/DDP (train/ship/Air)
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.