JIS G3521 SWRH47A Patented Spring Steel Wire

JIS G3521 SWRH47A Patented Spring Steel Wire
JIS G3521 SWRH47A Patented Spring Steel Wire JIS G3521 SWRH47A Patented Spring Steel Wire

Large Image :  JIS G3521 SWRH47A Patented Spring Steel Wire

Product Details:
Place of Origin: China
Brand Name: Fushun
Certification: ISO9001:2008
Model Number: SWRH47A
Payment & Shipping Terms:
Minimum Order Quantity: negotiable
Price: negotiable
Packaging Details: nylon/pallet/case
Delivery Time: 15-30 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 40,000tons/year

JIS G3521 SWRH47A Patented Spring Steel Wire

Description
Diameter: 0.1-15mm Form Of Delivery: A Coil (singles, Carriers Or Formers), Spools, Spoolless Cores Or As Straight Lengths.
Drawn Condition: Dry Drawn/paste Draw/gray Bright/wet Drawn/liquor Finished Heat Treatment: Patenting
Surface Condition: Bright /phosphate Coated /reddish /copper Plated/galvanised /zinc/aluminium Coated/yellow Coated/white (liquor Finished) Grade: SWRH47A
Classification: Patented Spring Steel Wire Standard: JIS G3521 SWRH47A
High Light:

JIS G3521 high carbon steel wire rod

,

10mm high carbon steel wire rod

,

SWRH47A high carbon wire rod

JIS G3521 SWRH47A Patented Spring Steel Wire

Supplying Size:
Diameter:0.1-15mm

 

Our Advantage
1. Stable linearity, good formability. Uniform and beautiful surface condition.
2. High plasticity and good fatigue resistance. And we provide Self-Inspection Reports and Raw-Material Test Certificates.
3. Professional anti-rust protective packaging. On time delivery, competitive price.
4. Large stock available, no MOQ requirement.

 

SWRH47A Patented Spring Steel Wire Chemical composition

C % Si% Mn% P % max. S % max.
0,44-0,51 0,10-0,30 0,30-0,60 0.030 0.030

 

Grade : SWRH47A Classification: Structural steel High carbon steel Standards: JIS G 3506 : High carbon steel wire rods Applications: High carbon steel wire rods to be used for the manufacture of hard drawn steel wires,oil tempered steel wires, hard drawn steel wires for prestressed concrete, galvanized wire strands, wipe ropes, etc.

 

SWRH47A Patented Spring Steel Wire Drawing condition

All cold drawn spring wire is commonly shaped by drawing. A distinction as to the method of drawing can be

made between:

1 dry drawn (d): drawn through pulverized lubricants such as soap, stearates or similar substances;

2 paste drawn (ps): drawn through very viscous greases of mineral oil base, tallow, synthetic waxes or similar substances;

3 gray bright (gr): drawn through rape oil, thin-bodied mineral oils or similar substances;

4 wet drawn (w): drawn through aqueous emulsions of greases or oil emulsions;

5 liquor finished (l): drawn through aqueous solutions with or without addition of metal salts.

 

SWRH47A Patented Spring Steel Wire Form of delivery

The wire shall be delivered in unit packages of a coil (singles, carriers or formers), spools, spoolless cores or as straight lengths. Unless otherwise agreed at the time of ordering, the form of delivery will be coils; straight lengths shall be supplied in bundles.

 

SWRH47A Patented Spring Steel Wire Coating and surface finish

The spring wire may be supplied phosphate coated (ph) either dry drawn or wet drawn, copper coated (cu), zinc (Z) or zinc/aluminium (ZA) coated.

Other coatings, considered as special, can be agreed between the purchaser and the supplier. If no specific surface finish is specified, the type of finish shall be at the manufacturers discretion. In addition the wire can be ordered with an oiled surface for all surface finishes.

 

SWRH47A Patented Spring Steel Wire Surface treatment

The surface for spring wire generally has a coating for facilitating wire drawing and spring forming.

Exceptionally the material will be uncoated. Common surface coatings are:

1 bright (b): without any special coating: standard borax coating or lime-coating may be applied;

2 phosphate coated (ph): the wire has been treated in a solution to form a metal-phosphate layer on the surface;

3 reddish (rd): the surface is covered with a thin copper, generally a conversion coating;

4 copper plated (cu): the surface is covered with a (uniform) thick copper coating;

5 galvanised (Z): the surface is covered with a zinc coating;

6 zinc/aluminium coated (ZA): the surface is covered with a Zn 95/Al 5 coating;

7 yellow coated (y): this applies only to liquor finished products whereby a mixture of tin salts and copper salts are added at the liquor finishing;

8 white (liquor finished) (wh): this applies to liquor finished products whereby tin salts are added for liquor finishing

 

The term “patented wire” refers to a particular process through which steel wire is strengthened to particular specifications, rather than an actual type of wire. Sometimes called “improved plow steel” or “extra improved plow steel” wire, patented wire is high-carbon, high-tensile steel wire that has been put through a special heat-treatment process for added durability and strength. For this reason, patented wire is popular for use in the manufacturing of wire rope, music wire and high tensile spring applications. Patented wire can be made to a variety of hardness levels, depending mainly on the carbon level in the steel prior to quenching. It is also available in a variety of diameter sizes.

 

SWRH47A Patented Spring Steel Wire Manufacture Process

wire drawn to size by cold deformation of a starting material that has been subjected to a thermal treatment of patenting, giving structure suitable for subsequent rolling or drawing.

Patenting HEAT TREATMENT consisting of AUSTENITIZING followed by COOLING under conditions suitable for producing the appropriate structures for subsequent wire-drawing or rolling. The medium in which the PATENTING takes place should be specified, for example air, lead bath etc.

 

SWRH47A Patented Spring Steel Wire Out of roundness

The difference between the maximum and minimum diameter of the wire at the same cross section shall not be more than 50 % of the total permissible deviation specified

 

SWRH47A Patented Spring Steel Wire Marking and packaging

Each unit shall be properly marked and identified so as to permit traceability and reference to the inspection documents.

The labels shall withstand normal handling and contact with oil; they shall show the information according to JIS G3521. Other information shall be the subject of an arrangement between the parties.

Wire shipments shall be suitably protected against mechanical damage and/or contamination during transport.

 