|Diameter:||0.1-15mm||Form Of Delivery:||A Coil (singles, Carriers Or Formers), Spools, Spoolless Cores Or As Straight Lengths.|
|Drawn Condition:||Dry Drawn/paste Draw/gray Bright/wet Drawn/liquor Finished||Heat Treatment:||Patenting|
|Surface Condition:||Bright /phosphate Coated /reddish /copper Plated/galvanised /zinc/aluminium Coated/yellow Coated/white (liquor Finished)||Grade:||SWRH32|
|SWRH42A:||Patented Spring Steel Wire||Standard:||JIS G3521 SWRH32|
JIS G3521 carbon steel spring wire,
60mm carbon steel spring wire,
1. Stable linearity, good formability. Uniform and beautiful surface condition.
2. High plasticity and good fatigue resistance. And we provide Self-Inspection Reports and Raw-Material Test Certificates.
3. Professional anti-rust protective packaging. On time delivery, competitive price.
4. Large stock available, no MOQ requirement.
SWRH32 Patented Spring Steel Wire Chemical composition
|C %||Si%||Mn%||P % max.||S % max.|
Grade : SWRH32 Classification: Structural steel High carbon steel Standards: JIS G 3506 : High carbon steel wire rods Applications: High carbon steel wire rods to be used for the manufacture of hard drawn steel wires,oil tempered steel wires, hard drawn steel wires for prestressed concrete, galvanized wire strands, wipe ropes, etc.
SWRH32 Patented Spring Steel Wire Drawing condition
All cold drawn spring wire is commonly shaped by drawing. A distinction as to the method of drawing can be
1 dry drawn (d): drawn through pulverized lubricants such as soap, stearates or similar substances;
2 paste drawn (ps): drawn through very viscous greases of mineral oil base, tallow, synthetic waxes or similar substances;
3 gray bright (gr): drawn through rape oil, thin-bodied mineral oils or similar substances;
4 wet drawn (w): drawn through aqueous emulsions of greases or oil emulsions;
5 liquor finished (l): drawn through aqueous solutions with or without addition of metal salts.
SWRH32 Patented Spring Steel Wire Surface treatment
The surface for spring wire generally has a coating for facilitating wire drawing and spring forming.
Exceptionally the material will be uncoated. Common surface coatings are:
1 bright (b): without any special coating: standard borax coating or lime-coating may be applied;
2 phosphate coated (ph): the wire has been treated in a solution to form a metal-phosphate layer on the surface;
3 reddish (rd): the surface is covered with a thin copper, generally a conversion coating;
4 copper plated (cu): the surface is covered with a (uniform) thick copper coating;
5 galvanised (Z): the surface is covered with a zinc coating;
6 zinc/aluminium coated (ZA): the surface is covered with a Zn 95/Al 5 coating;
7 yellow coated (y): this applies only to liquor finished products whereby a mixture of tin salts and copper salts are added at the liquor finishing;
8 white (liquor finished) (wh): this applies to liquor finished products whereby tin salts are added for liquor finishing
SWRH32 Patented Spring Steel Wire Surface quality
The surface of the wire shall be smooth and as free as possible from grooves, tears, rust and other surface defects, which have a noticeable adverse effect on the application of the wire.
In the case of zinc or zinc/aluminium coated spring wire the amount of zinc or zinc/aluminium on the wire surface shall satisfy the minimum values specified
Patented Wire is a standard grade music wire that has been conditioned for spring and wire rope applications where strength and high tensile are needed. Patenting is a heat treatment process that improves the durability and strength of the wire. The process involves an in-line heat treatment at 970 degrees Fahrenheit and then cooled in a variety of mediums including air and lead.
SWRH32 Patented Spring Steel Wire Manufacture Process
wire drawn to size by cold deformation of a starting material that has been subjected to a thermal treatment of patenting, giving structure suitable for subsequent rolling or drawing.
Patenting HEAT TREATMENT consisting of AUSTENITIZING followed by COOLING under conditions suitable for producing the appropriate structures for subsequent wire-drawing or rolling. The medium in which the PATENTING takes place should be specified, for example air, lead bath etc.
SWRH32 Patented Spring Steel Wire Out of roundness
The difference between the maximum and minimum diameter of the wire at the same cross section shall not be more than 50 % of the total permissible deviation specified
SWRH32 Patented Spring Steel Wire Marking and packaging
Each unit shall be properly marked and identified so as to permit traceability and reference to the inspection documents.
The labels shall withstand normal handling and contact with oil; they shall show the information according to JIS G3521. Other information shall be the subject of an arrangement between the parties.
Wire shipments shall be suitably protected against mechanical damage and/or contamination during transport.