Product Details:
|
| Grade: | C86D C86D2 | Feature: | High Carbon |
|---|---|---|---|
| Form: | Wires | Heat Treatment: | Patenting |
| Surface Condition: | Bright /phosphate Coated /reddish /copper Plated/galvanised /zinc/aluminium Coated/yellow Coated/white (liquor Finished) | EN 10016-2: | C86D |
| EN 10016-4: | C86D2 | Standard: | BS EN 10207-1 C86D C86D2 |
| High Light: | ASTM A510 spring wire steel,C86D2 spring wire steel,0.8 mm stainless steel wire |
||
Supplying Size:
Diameter:0.1-15mm
Our Advantage
1. Stable linearity, good formability. Uniform and beautiful surface condition.
2. High plasticity and good fatigue resistance. And we provide Self-Inspection Reports and Raw-Material Test Certificates.
3. Professional anti-rust protective packaging. On time delivery, competitive price.
4. Large stock available, no MOQ requirement.
EN 10016-2: 1994 Non-alloy steel rods for drawing and/or cold rolling. Specific requirements for general purpose rod
EN 10016-4: 1994 Non-alloy steel rods for drawing and/or cold rolling. Specific requirements for general purpose rod
BS EN 10270-1 2011 Steel wire for mechanical springs Patented cold drawn unalloyed spring steel wire
| Steel name | Steel number | C % | Si% | Mn% | P % max. | S % max. | Cr % max. | Ni % max. | Mo % max. | Cl% max. | Al % max. | N% max. |
| C86D | 1.0616 | 0,83-0,88 | 0,10-0,30 | 0,50-0,80 | 35 | 35 | 0.15 | 0.2 | 0.05 | 0.25 | 0.01 | |
| C86D2 | 1.1265 | 0,84-0,88 | 0,10-0,30 | 0,50-0,70 | 0,020 | 0,025 | 0,10 | 0,10 | 0,02 | 0,15 | 0,01 | 0,007 |
C86D C86D2 High Carbon Spring Steel Wire Drawing condition
All cold drawn spring wire is commonly shaped by drawing. A distinction as to the method of drawing can be
made between:
1 dry drawn (d): drawn through pulverized lubricants such as soap, stearates or similar substances;
2 paste drawn (ps): drawn through very viscous greases of mineral oil base, tallow, synthetic waxes or similar substances;
3 gray bright (gr): drawn through rape oil, thin-bodied mineral oils or similar substances;
4 wet drawn (w): drawn through aqueous emulsions of greases or oil emulsions;
5 liquor finished (l): drawn through aqueous solutions with or without addition of metal salts.
The wire shall be delivered in unit packages of a coil (singles, carriers or formers), spools, spoolless cores or as straight lengths. Unless otherwise agreed at the time of ordering, the form of delivery will be coils; straight lengths shall be supplied in bundles.
The spring wire may be supplied phosphate coated (ph) either dry drawn or wet drawn, copper coated (cu), zinc (Z) or zinc/aluminium (ZA) coated.
Other coatings, considered as special, can be agreed between the purchaser and the supplier. If no specific surface finish is specified, the type of finish shall be at the manufacturers discretion. In addition the wire can be ordered with an oiled surface for all surface finishes.
High-carbon spring steels are the most commonly used of all springs materials. They will meet your spring steel material specification in preference to others, despite being the least expensive. High Carbon spring wires are readily available, easily worked, and most popular. These materials are not satisfactory for high or low temperatures or for shock or impact loading.We're ISO 9001:2008-certified spring manufacturer dedicated to supplying our customers with high-performance spring products on time and at a competitive price. Hard-drawn spring steel wire, or HDMB spring wire, is manufactured using a cold-drawing process. During this activity, the wire being worked is coated in oil and pulled through one or more dies to reduce the wire width. One of the most economical and versatile steel wire types, hard-drawn wire is perfect for a range of general-purpose applications.
The surface of the wire shall be smooth and as free as possible from grooves, tears, rust and other surface defects, which have a noticeable adverse effect on the application of the wire.
In the case of zinc or zinc/aluminium coated spring wire the amount of zinc or zinc/aluminium on the wire surface shall satisfy the minimum values specified
High carbon steel springs are very popular due to their econimcal, strong, and durable nature. The Fushun is equipped with the knowledge and expertise to facilitate in your selection of the perfect high carbon steel springs for your project, customizing the springs to your exact specifications. Fushun Wire Spring manufactures custom springs using many types of high carbon steel wire, including oil tempered steel wire. We specialize in providing each client with a custom spring that matches your exact application requirements, leveraging over 85 years of experience producing springs for industrial applications. Our staff is available to assist you in selecting the best high carbon steel for your application and will manufacture your springs to specifications and the highest quality standards. You can be assured that your springs will be delivered to you fast and ready for your production line. High carbon spring steel wires are the most popular steel wires used when manufacturing springs. They are economical, strong, and durable.
The difference between the maximum and minimum diameter of the wire at the same cross section shall not be more than 50 % of the total permissible deviation specified
The purchaser shall clearly state in his enquiry or order the product and following information:
a) the desired quantity;
b) the term spring steel wire or straightened and cut lengths;
c) the number of this European standard: EN 10270-1;
d) the steel grade
e) the nominal wire diameter selected from Table 3 and for cut length the length and the length tolerance class
f) the coating indicated by its abbreviation and surface finish
g) the form of delivery and unit mass
h) the type of inspection document;
i) any particular agreement
wire drawn to size by cold deformation of a starting material that has been subjected to a thermal treatment of patenting, giving structure suitable for subsequent rolling or drawing.
Patenting HEAT TREATMENT consisting of AUSTENITIZING followed by COOLING under conditions suitable for producing the appropriate structures for subsequent wire-drawing or rolling. The medium in which the PATENTING takes place should be specified, for example air, lead bath etc.
Each unit shall be properly marked and identified so as to permit traceability and reference to the inspection documents.
The labels shall withstand normal handling and contact with oil; they shall show the information according to EN 10270-1. Other information shall be the subject of an arrangement between the parties.
Wire shipments shall be suitably protected against mechanical damage and/or contamination during transport.