|Thickness:||1 To 8 Mm||Width:||10 To 400 Mm|
|Delivery Condition:||Quenched Tempered(+QT)||Surface Condition:||Polished Blue|
|EN Grade:||C75S Steel||EN Number:||1.1248 Steel|
|Supply Form:||Coil And Plate||Standard:||BS EN 10132-4 C75S 1.1248|
3mm Stainless Spring Steel Strip,
1.1248 Stainless Spring Steel Strip,
BS EN C75S 1.1248 Blue Spring Steel Strips
Grade : C75S Number: 1.1248
Dimensions and tolerances
Thickness: 1 to 8 mm; Tolerances: +/- 0.008 to 0.11 mm
Width: 10 to 400 mm; Tolerances: +/- 0.15 to 0.60
*accept nonstandard size, please contact with our sales.
1. Precise thickness, uniform hardness. Bright surface, smooth edge.
2. High flatness of board surface, high performance after multiple bending.
3. No cracking after stamping, and the quality is stable. And we provide Self-Inspection Reports and Raw-Material Test Certificates.
4. Professional anti-rust protective packaging. On time delivery, competitive price.
5. Large stock available, no MOQ requirement
C75S 1.1248 Blue Steel Strips Chemical composition
|name||number||C||Si||Mn||P max.||S max.||Cr||Mo max.||Ni|
|C75S||1.1248||0,70 to 0,80||0,15 to 0,35||0,60 to 0,90||0,025||0,025||max. 0,40||0,10||max. 0,40|
C75S 1.1248 Blue Steel Strips Mechanical properties
|Steel designation||delivery condition|
|annealed (+A) or annealed and skin passed (+LC)||cold rolled (+CR)||quenched and tempered (+QT)|
|name||number||Proof strength max. Mpa||Tensile strength max. Mpa||Elongation % min.||HV max.||Tensile strength max. Mpa||HV max.||Tensile strength Mpa||HV|
|C75S||1.1248||510||640||15||200||1170||320||1 200 to 1 900||370 to 580|
C75S 1.1248 Blue Steel Strips Delivery condition
Cold rolled narrow steel strip covered by EN10132-4 shall be supplied in one of the following delivery conditions:
NOTE The delivery condition-annealed to achieve spheroidized carbides(+AC)-may be agreed. In such cases, limits on spheroidization and mechanical properties may also be agreed at the time of enquiry and order.
C75S 1.1248 Blue Steel Strips Decarburization
For silicon alloyed steels, decarburization shall not exceed 3% of the material thickness per side,for non silicon alloyed steels, decarburization shall not exceed 2% of the material thickness per side when measure data distance of 5mm from the stripe edge
C75S 1.1248 Blue Steel Strips Surface finish
The surface finish of cold rolled narrow steel strip shall be bright as produced by rolling and annealing in a controlled atmosphere.
The surface finishes of quenched and tempered cold rolled strip are as follows:
1 grey/blue oxide finish:unpolished;
2 brigth tempered:unpolished
3 polished: obtained by fine grinding, abrasive brushing or other processes;
4 polished and coloured:blue or yellow colour obtained by oxidization by heat treatment.
C75S 1.1248 Blue Steel Strips Mandatory information
The following information shall be supplied by the purchaser at the time of enquiry and order to enable the supplier to comply with the requirements of this European Standard:
a) the quantity to be delivered;
b) the designation of the product form (cold rolled narrow strip);
c) the number of the dimensional standard (EN 10140);
d) the dimensions and tolerances on dimensions and shape and, if applicable, letters
denoting relevant special tolerances;
e)the number of this European Standard including the number of the relevant part;
f) steel name or steel number
g) the delivery condition
h) if required, the type of inspection document in accordance with EN 10204.
As a spring steel, it is used for medium-weight machine parts such as bolts and bucket links, rolls, molding boards, agricultural machinery parts, press plates and ball mills, press rods, and briquette presses. Non-weldable steel, resistant to temper embrittlement, prone to decarburization and oxidation during heat treatment.
high carbon steel blue tempered spring steel strip is harder, less bendable, and has a higher degree of spring back. Finished products made from this material have better edge retention, which correlates to the material's other properties. blue spring steel strip is used widely in the manufacture of springs, prominently in automotive and industrial suspension applications. It is a high carbon steel with a very high yield strength. This material allows objects made of spring steel to return to their original shape despite significant deflection or twisting.
75 steel - C75S - Carbon spring steel with low hardening capacity for lightweight springs for oil hardening. It is characterized by resistance to abrasion and high strength. Used for low-loaded springs and springs, spring parts, clock springs, saws for cutting stones in the form of tapes and sheets.
C75S 1.1248 Blue Steel Strips Inspection and testing