BS EN 10132-4 C85S 1.1269 Quenched Tempered Spring Steel Strip

BS EN 10132-4 C85S 1.1269 Quenched Tempered Spring steel strip

C85S 1.1269 Quenched Tempered Strip Dimensions and tolerances

Thickness: 1 to 8mm; Tolerances: +/- 0.008 to 0.11 mm

Width: 10 to 400mm; Tolerances: +/- 0.15 to 0.60

Chemical composition

C85S 1.1269 Quenched Tempered Strip Mechanical properties

C85S 1.1269 Quenched Tempered Strip Mandatory information

The following information shall be supplied by the purchaser at the time of enquiry and order to enable the supplier to comply with the requirements of this European Standard:

a) the quantity to be delivered;

b) the designation of the product form (cold rolled narrow strip);

c) the number of the dimensional standard (EN 10140);

d) the dimensions and tolerances on dimensions and shape and, if applicable, letters

denoting relevant special tolerances;

e)the number of this European Standard including the number of the relevant part;

f) steel name or steel number

g) the delivery condition

h) if required, the type of inspection document in accordance with EN 10204.

C85S 1.1269 Quenched Tempered Strip Delivery condition

Cold rolled narrow steel strip covered by EN10132-4 shall be supplied in one of the following delivery conditions:

-annealed or annealed and skin passed(+A or +LC);

-cold rolled(+CR);

-quenched and tempered(+QT).

NOTE The delivery condition-annealed to achieve spheroidized carbides(+AC)-may be agreed. In such cases, limits on spheroidization and mechanical properties may also be agreed at the time of enquiry and order.

C85S 1.1269 Quenched Tempered Strip Decarburization

For silicon alloyed steels, decarburization shall not exceed 3% of the material thickness per side,for non silicon alloyed steels, decarburization shall not exceed 2% of the material thickness per side when measure data distance of 5mm from the stripe edge

C85S, 1.1269, AISI 1086 specification and application : C85S is non-alloyed carbon structural steel with low hardening capacity for oil hardening for low-duty, periodically operating springs, springs and spring elements, immune to the temper brittleness. It is characterized by its high hardness and abrasion resistance, while maintaining high strength. It is used for flat and spiral springs, machine parts or saws of all kinds for cutting.

Grade 85 and C85S steel are mainly used as steel for ball mills, press plates, stone saws, wire for steel ropes, briquetting press parts. C85S and 85 steels are non-weldable and resistant to corrosive environments due to their high carbon content and low levels of alloying additives. During heat treatment steel is vulnerable to decarburization and oxidation.

The steel C85S is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm. The cold-rolled steel strip for springs possess a very high precision of measurements and very good state of the surface.

Hardened and Tempered Steel Strip (also known as hardened and tempered High carbon steel strip or, hardened and tempered carbon spring steel strip) is the basic raw material from which many different components are made, substantially being spring-type applications ranging from clutch plate segments to washers, retractor springs and even to tree springs in riding saddles and traditional clock springs. These strip products are a specialty of the Company and considerable plant development has taken place in recent years to facilitate a very wide range of dimensions, mechanical properties and coil weights. Hardened and Tempered Steel Strip gauges of between 0.10mm and 2.00mm can be processed and, depending on the appropriate combination to suit the process equipment, strip widths of between 4.76mm to 240mm are produced. The facilities also allow up to 2000kg coils to be produced though most are well below this, being governed by a very approximate relationship of 100kg per 25mm of width.

The surface finish of Hardened and Tempered Steel Strip products is not too critical in general engineering applications where the normal blue-black (also known as blue-grey) oxidized finish from the heat treatment is satisfactory. By control of the atmospheres in the furnaces non-oxidised surfaces can also be produced, on a selected basis, and alternatively, steels can be satin or bright polished were needed, these finishes being as much for cosmetic reasons as for engineering purposes.

C85S 1.1269 Quenched Tempered Strip Surface finish

The surface finish of cold rolled narrow steel strip shall be bright as produced by rolling and annealing in a controlled atmosphere.

The surface finishes of quenched and tempered cold rolled strip are as follows:

1 grey/blue oxide finish:unpolished;

2 brigth tempered:unpolished

3 polished: obtained by fine grinding, abrasive brushing or other processes;

4 polished and coloured:blue or yellow colour obtained by oxidization by heat

treatment.

High carbon steel is an ideal material for custom flat springs, custom clips, and custom sheet metal stampings. High Carbon Steel Strips combines ease of fabrication with good strength and surface finish, is valued for its strength properties and operates at significantly higher levels than the mild steel grades. High carbon steel strip can be finished to meet the needs of a wide range of products. Where tensile strength and hardness are required, High Carbon steels are the material of choice. High Carbon Steel Strips Grades : C60, C65, C70, C75, C85, HC-14, En 42 J, C-98, C-100, C-124, HC21 etc. We offer spring steel strip in various shapes and sizes according to your final uses. These have excellent hardens property and high yield strength. Clients can avail these at competitive prices.