|Thickness:||1 To 8 Mm||Width:||10 To 400 Mm|
|Delivery Condition:||Quenched Hardened Tempered||Surface Condition:||1 Grey/blue Oxide Finish:unpolished;2 Bright Tempered:unpolished; 3 Polished: 4 Polished And Coloured:blue Or Yellow Colour|
|Form:||Steel Strips||Standard:||Bs EN 10132-4 C67S 1.1231|
High Carbon Tempered Spring Steel Strip,
0.1mm Tempered Spring Steel Strip,
BS EN 10132-4 C67S 1.1231 Quenched Tempered Spring steel strip
Dimensions and tolerances
Thickness: 1 to 8 mm; Tolerances: +/- 0.008 to 0.11 mm
Width: 10 to 400 mm; Tolerances: +/- 0.15 to 0.60
1. Precise thickness, uniform hardness. Bright surface, smooth edge.
2. High flatness of board surface, high performance after multiple bending.
3. No cracking after stamping, and the quality is stable. And we provide Self-Inspection Reports and Raw-Material Test Certificates.
4. Professional anti-rust protective packaging. On time delivery, competitive price.
5. Large stock available, no MOQ requirement
C67S 1.1231 Quenched Tempered Strip Chemical composition
|name||number||C||Si||Mn||P max.||S max.||Cr||Mo max.||Ni|
|C67S||1.1231||0,65 to 0,73||0,15 to 0,35||0,60 to 0,90||0,025||0,025||max. 0,40||0,10||max. 0,40|
C67S 1.1231 Quenched Tempered Strip Mechanical properties
|Steel designation||delivery condition|
|annealed (+A) or annealed and skin passed (+LC)||cold rolled (+CR)||quenched and tempered (+QT)|
|name||number||Proof strength max. Mpa||Tensile strength max. Mpa||Elongation % min.||HV max.||Tensile strength max. Mpa||HV max.||Tensile strength Mpa||HV|
|C67S||1.1231||510||640||16||200||1140||315||1 200 to 1 900||370 to 580|
C67S 1.1231 Quenched Tempered Strip Mandatory information
The following information shall be supplied by the purchaser at the time of enquiry and order to enable the supplier to comply with the requirements of this European Standard:
a) the quantity to be delivered;
b) the designation of the product form (cold rolled narrow strip);
c) the number of the dimensional standard (EN 10140);
d) the dimensions and tolerances on dimensions and shape and, if applicable, letters
denoting relevant special tolerances;
e)the number of this European Standard including the number of the relevant part;
f) steel name or steel number
g) the delivery condition
h) if required, the type of inspection document in accordance with EN 10204.
C67S 1.1231 Quenched Tempered Strip Delivery condition
Cold rolled narrow steel strip covered by EN10132-4 shall be supplied in one of the following delivery conditions:
-annealed or annealed and skin passed(+A or +LC);
-quenched and tempered(+QT).
NOTE The delivery condition-annealed to achieve spheroidized carbides(+AC)-may be agreed. In such cases, limits on spheroidization and mechanical properties may also be agreed at the time of enquiry and order.
C67S 1.1231 Quenched Tempered Strip Decarburization
For silicon alloyed steels, decarburization shall not exceed 3% of the material thickness per side,for non silicon alloyed steels, decarburization shall not exceed 2% of the material thickness per side when measure data distance of 5mm from the stripe edge
Material No.: C67S 1.1231 German standard: DIN EN 10132 International steel grades: SAE:1070 JIS: S70CM Unalloyed steel for springs as belleville washers, spring plates and stabilizer bars for motor vehicles Hot forming and heat treatment: Forging or hot rolling: Normalising: Soft annealing: Hardening: 1100 - 800°C 810 - 840°C/air 680 - 710°C/furnace 815 - 845°C/oil min. 59 HRC or 670 HV as quenched
The steel C60S is used as cold rolled strip for springs and special applications in thicknesses of up to 6 mm and as tempered cold strip in thicknesses from 0.30 to 3.00 mm. The cold-rolled steel strip for springs possess a very high precision of measurements and very good state of the surface.
Hardened and Tempered Steel Strip (also known as hardened and tempered High carbon steel strip or, hardened and tempered carbon spring steel strip) is the basic raw material from which many different components are made, substantially being spring-type applications ranging from clutch plate segments to washers, retractor springs and even to tree springs in riding saddles and traditional clock springs. These strip products are a specialty of the Company and considerable plant development has taken place in recent years to facilitate a very wide range of dimensions, mechanical properties and coil weights. Hardened and Tempered Steel Strip gauges of between 0.10mm and 2.00mm can be processed and, depending on the appropriate combination to suit the process equipment, strip widths of between 4.76mm to 240mm are produced. The facilities also allow up to 2000kg coils to be produced though most are well below this, being governed by a very approximate relationship of 100kg per 25mm of width.
The surface finish of Hardened and Tempered Steel Strip products is not too critical in general engineering applications where the normal blue-black (also known as blue-grey) oxidized finish from the heat treatment is satisfactory. By control of the atmospheres in the furnaces non-oxidised surfaces can also be produced, on a selected basis, and alternatively, steels can be satin or bright polished were needed, these finishes being as much for cosmetic reasons as for engineering purposes.
C67S 1.1231 Quenched Tempered Strip Surface finish
The surface finish of cold rolled narrow steel strip shall be bright as produced by rolling and annealing in a controlled atmosphere.
The surface finishes of quenched and tempered cold rolled strip are as follows:
1 grey/blue oxide finish:unpolished;
2 brigth tempered:unpolished
3 polished: obtained by fine grinding, abrasive brushing or other processes;
4 polished and coloured:blue or yellow colour obtained by oxidization by heat
C67S 1.1231 Quenched Tempered Strip Inspection and testing
verification of the dimensions
visual examination of the surface quality
Extent of testing
Tensile and bending tests
Tolerances on shape