Send Message
Home ProductsOthers

BS DIN EN C82D C82D2 Patented Steel Wire

All Products

Process

(4)

Industry

(2)

Materials

(2)

Others

(305)
Certification
China Hunan Fushun Metal Co., Ltd. certification
China Hunan Fushun Metal Co., Ltd. certification
I'm Online Chat Now

BS DIN EN C82D C82D2 Patented Steel Wire

BS DIN EN C82D C82D2 Patented Steel Wire
BS DIN EN C82D C82D2 Patented Steel Wire BS DIN EN C82D C82D2 Patented Steel Wire

Large Image :  BS DIN EN C82D C82D2 Patented Steel Wire

Product Details:
Place of Origin: China
Brand Name: Fushun
Certification: ISO9001:2008
Model Number: C82D C82D2
Payment & Shipping Terms:
Minimum Order Quantity: 0.1-0.5-1 tons
Packaging Details: nylon/pallet/case
Delivery Time: 15-30 days
Payment Terms: L/C, T/T, Western Union
Supply Ability: 40,000tons/year

BS DIN EN C82D C82D2 Patented Steel Wire

Description
Diameter: 0.1-15mm Form Of Delivery: A Coil (singles, Carriers Or Formers), Spools, Spoolless Cores Or As Straight Lengths.
Drawn Condition: Dry Drawn/paste Draw/gray Bright/wet Drawn/liquor Finished Heat Treatment: Patenting
Surface Condition: Bright /phosphate Coated /reddish /copper Plated/galvanised /zinc/aluminium Coated/yellow Coated/white (liquor Finished) EN 10016-2: C82D C82D2
EN 10016-4: C82D C82D2 Standard: BS EN 10270-1 C82D C82D2
High Light:

C82D Patented Steel Wire

,

Fushun Patented Steel Wire

,

C82D2

C82D C82D2 Spring Steel Wire 

EN 10016-2: 1994 Non-alloy steel rods for drawing and/or cold rolling. Specific requirements for general purpose rod

EN 10016-4: 1994 Non-alloy steel rods for drawing and/or cold rolling. Specific requirements for general purpose rod

BS EN 10270-1 2011 Steel wire for mechanical springs Patented cold drawn unalloyed spring steel wire

 

Grade : C82D
Number: 1.0626
Classification: Non-alloy steel
Standard:
EN 10016-2: 1995 Non-alloy steel rods for drawing and/or cold rolling. Specific requirements for general purpose rod
 
Equivalent Materials
GB C82DGB U53822IS IS1835IS IS7904ISO C82DJIS SWRH82AJIS SWRH82BDIN D83-2ASTM A510 Grade 1078UNS G10780IS nanKS HSWR82ADIN 1.0626DIN D 83-2DIN C82DAFNOR C82DBS C82DAISI 1078SAE 1078JIS SWRH82EN 1.0626GB U59823GB/T C82DGB/T U53822GB/T U59823
 

Supplying Size:
Diameter:0.1-15mm

 

Our Advantage
1. Stable linearity, good formability. Uniform and beautiful surface condition.
2. High plasticity and good fatigue resistance. And we provide Self-Inspection Reports and Raw-Material Test Certificates.
3. Professional anti-rust protective packaging. On time delivery, competitive price.
4. Large stock available, no MOQ requirement.

C82D C82D2 Spring Steel Wire Chemical composition

Steel name Steel number C % Si% Mn% P % max. S % max. Cr % max. Ni % max. Mo % max. Cl% max. Al % max. N% max.
C82D 1.0626 0,80-0,85 0,10-0,30 0,50-0,80 35 35 0.15 0.2 0.05 0.25 0.01  
C82D2 1.1262 0,80-0,84 0,10-0,30 0,50-0,70 0,020 0,025 0,10 0,10 0,02 0,15 0,01 0,007

 

C82D C82D2 Spring Steel Wire Drawing condition

All cold drawn spring wire is commonly shaped by drawing. A distinction as to the method of drawing can be

made between:

1 dry drawn (d): drawn through pulverized lubricants such as soap, stearates or similar substances;

2 paste drawn (ps): drawn through very viscous greases of mineral oil base, tallow, synthetic waxes or similar substances;

3 gray bright (gr): drawn through rape oil, thin-bodied mineral oils or similar substances;

4 wet drawn (w): drawn through aqueous emulsions of greases or oil emulsions;

5 liquor finished (l): drawn through aqueous solutions with or without addition of metal salts.

 

C82D C82D2 Spring Steel Wire Form of delivery

The wire shall be delivered in unit packages of a coil (singles, carriers or formers), spools, spoolless cores or as straight lengths. Unless otherwise agreed at the time of ordering, the form of delivery will be coils; straight lengths shall be supplied in bundles.

 

C82D C82D2 Spring Steel Wire Coating and surface finish

The spring wire may be supplied phosphate coated (ph) either dry drawn or wet drawn, copper coated (cu), zinc (Z) or zinc/aluminium (ZA) coated.

Other coatings, considered as special, can be agreed between the purchaser and the supplier. If no specific surface finish is specified, the type of finish shall be at the manufacturers discretion. In addition the wire can be ordered with an oiled surface for all surface finishes.

 

C82D C82D2 Spring Steel Wire Surface treatment

The surface for spring wire generally has a coating for facilitating wire drawing and spring forming.

Exceptionally the material will be uncoated. Common surface coatings are:

1 bright (b): without any special coating: standard borax coating or lime-coating may be applied;

2 phosphate coated (ph): the wire has been treated in a solution to form a metal-phosphate layer on the surface;

3 reddish (rd): the surface is covered with a thin copper, generally a conversion coating;

4 copper plated (cu): the surface is covered with a (uniform) thick copper coating;

5 galvanised (Z): the surface is covered with a zinc coating;

6 zinc/aluminium coated (ZA): the surface is covered with a Zn 95/Al 5 coating;

7 yellow coated (y): this applies only to liquor finished products whereby a mixture of tin salts and copper salts are added at the liquor finishing;

8 white (liquor finished) (wh): this applies to liquor finished products whereby tin salts are added for liquor finishing

 

C82D C82D2 Spring Steel Wire Surface quality

The surface of the wire shall be smooth and as free as possible from grooves, tears, rust and other surface defects, which have a noticeable adverse effect on the application of the wire.

In the case of zinc or zinc/aluminium coated spring wire the amount of zinc or zinc/aluminium on the wire surface shall satisfy the minimum values specified

 

The term “patented wire” refers to a particular process through which steel wire is strengthened to particular specifications, rather than an actual type of wire. Sometimes called “improved plow steel” or “extra improved plow steel” wire, patented wire is high-carbon, high-tensile steel wire that has been put through a special heat-treatment process for added durability and strength. For this reason, patented wire is popular for use in the manufacturing of wire rope, music wire and high tensile spring applications. Patented wire can be made to a variety of hardness levels, depending mainly on the carbon level in the steel prior to quenching. It is also available in a variety of diameter sizes.

C82D C82D2 Spring Steel Wire Manufacture Process

wire drawn to size by cold deformation of a starting material that has been subjected to a thermal treatment of patenting, giving structure suitable for subsequent rolling or drawing.

Patenting HEAT TREATMENT consisting of AUSTENITIZING followed by COOLING under conditions suitable for producing the appropriate structures for subsequent wire-drawing or rolling. The medium in which the PATENTING takes place should be specified, for example air, lead bath etc.

 

C82D C82D2 Spring Steel Wire Out of roundness

The difference between the maximum and minimum diameter of the wire at the same cross section shall not be more than 50 % of the total permissible deviation specified

 

C82D C82D2 Spring Steel Wire Marking and packaging

Each unit shall be properly marked and identified so as to permit traceability and reference to the inspection documents.

The labels shall withstand normal handling and contact with oil; they shall show the information according to EN 10270-1. Other information shall be the subject of an arrangement between the parties.

Wire shipments shall be suitably protected against mechanical damage and/or contamination during transport.

BS DIN EN C82D C82D2 Patented Steel Wire 0

Contact Details
Hunan Fushun Metal Co., Ltd.

Contact Person: Ms. Florence Tang

Fax: 86-731-89853933

Send your inquiry directly to us (0 / 3000)